Lembaran Stainless Steel 201 untuk pelanggan
Mar 16, 2026
Tinggalkan pesan
| Standar | ASTM A240, EN 10088-2, GB/T 3280 |
|---|---|
| Nilai | 1.4372, SUS201, X12CrMnNiN17-7-5, Z12CMN17-07Az |
| Panjang | 2000 mm-6000 mm (78,74-236,22 inci), Disesuaikan |
| Lebar Penuh | 1000 mm-2000 mm (39,37-78,74 inci), Disesuaikan |
| Ketebalan | 0,3 mm-6 mm (0,012-0,24 inci), Disesuaikan |
| Permukaan Selesai | 2B, 8K, BA, dll., HL, No.1, No.4 |
| Teknik | Ditarik Dingin, Digulung Dingin, Digulung Panas |
| Membentuk | Coil, Cold Rolled Sheet, Embossed Sheets, dll., Flat Plate & Sheet, Hot Rolled Sheet, Perforated Sheets, Plate, Polished Sheets, Strip, Textured Sheets |
Komposisi Kimia
| Elemen | Karbon (C) | Mangan (Mn) | Silikon (Si) | Fosfor (P) | Belerang (S) | Kromium (Cr) | Nikel (Ni) | Nitrogen (N) |
|---|
| Komposisi (%) | 0,15 maks | 5.5-7.5 | 1,0 maks | 0,06 maks | 0,03 maks | 16.0-18.0 | 3.5-5.5 | 0,25 maks |
Sifat Mekanik
| Properti | Satuan Metrik | Satuan Kekaisaran |
|---|
| Kekuatan Tarik | 655 – 860 MPa | 95 – 125xi |
| Kekuatan Hasil | 450MPa | 65ksi |
| Kekerasan Vickers | 230 – 270 HV | 230 – 270 HV |
| Kekerasan Brinell | 200 – 250 HB | 200 – 250 HB |
| Kekerasan Rockwell | 50 – 56 HRC | 50 – 56 HRC |
| Pemanjangan | 20% | 20% |
| Modulus Elastis | 200 IPK | 29x10^6 psi |